海洋構造物の劣化とその防除に関する研究(第3報) : 各種塗料による金属材料の腐食および生物付着の防除について
https://kindai.repo.nii.ac.jp/records/5139
https://kindai.repo.nii.ac.jp/records/5139584d8fb7-9f33-46e9-a555-edb05599c0f3
| 名前 / ファイル | ライセンス | アクション |
|---|---|---|
AN00064044-19760315-0057.pdf (2.4 MB)
|
|
| Item type | ☆紀要論文 / Departmental Bulletin Paper(1) | |||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| 公開日 | 2008-03-18 | |||||||||||||||||
| タイトル | ||||||||||||||||||
| タイトル | 海洋構造物の劣化とその防除に関する研究(第3報) : 各種塗料による金属材料の腐食および生物付着の防除について | |||||||||||||||||
| タイトル | ||||||||||||||||||
| タイトル | Studies on the Deterioration and its Prevention of Marine Structure (III) : On the Effects of Various Paints in order to Prevent Corrosions and Fouling Organisms on Metal Materials in the sea | |||||||||||||||||
| 言語 | en | |||||||||||||||||
| 著者 |
布施, 五郎
× 布施, 五郎
× 田中, 裕美
× 竹内, 孝常
|
|||||||||||||||||
| 言語 | ||||||||||||||||||
| 言語 | jpn | |||||||||||||||||
| 資源タイプ | ||||||||||||||||||
| 資源タイプ識別子 | http://purl.org/coar/resource_type/c_6501 | |||||||||||||||||
| 資源タイプ | departmental bulletin paper | |||||||||||||||||
| 著者(英) | ||||||||||||||||||
| 言語 | en | |||||||||||||||||
| 値 | Fuse, Goro | |||||||||||||||||
| 著者(英) | ||||||||||||||||||
| 言語 | en | |||||||||||||||||
| 値 | Tanaka, Hiromi | |||||||||||||||||
| 著者(英) | ||||||||||||||||||
| 言語 | en | |||||||||||||||||
| 値 | Takeuchi, Takatsune | |||||||||||||||||
| 著者 所属 | ||||||||||||||||||
| 値 | 近畿大学農学部農芸化学科林産化学研究室 | |||||||||||||||||
| 著者 所属 | ||||||||||||||||||
| 値 | 近畿大学農学部農芸化学科林産化学研究室 | |||||||||||||||||
| 著者 所属 | ||||||||||||||||||
| 値 | 東洋木材防腐（株）研究開発部 | |||||||||||||||||
| 著者所属(翻訳) | ||||||||||||||||||
| 値 | Laboratory of Forest Products Chemistry, Department of Agricultural Chemistry, Faculty of Agriculture, Kinki University | |||||||||||||||||
| 著者所属(翻訳) | ||||||||||||||||||
| 値 | Laboratory of Forest Products Chemistry, Department of Agricultural Chemistry, Faculty of Agriculture, Kinki University | |||||||||||||||||
| 著者所属(翻訳) | ||||||||||||||||||
| 値 | Department of Research & Development, Toyo Wood Preservation Co., Ltd. | |||||||||||||||||
| 版 | ||||||||||||||||||
| 出版タイプ | NA | |||||||||||||||||
| 出版タイプResource | http://purl.org/coar/version/c_be7fb7dd8ff6fe43 | |||||||||||||||||
| 出版者 名前 | ||||||||||||||||||
| 出版者 | 近畿大学農学部 | |||||||||||||||||
| 書誌情報 |
近畿大学農学部紀要 en : Memoirs of the Faculty of Agriculture of Kinki University 号 9, p. 57-81, 発行日 1976-01-01 |
|||||||||||||||||
| ISSN | ||||||||||||||||||
| 収録物識別子タイプ | ISSN | |||||||||||||||||
| 収録物識別子 | 04538889 | |||||||||||||||||
| 抄録 | ||||||||||||||||||
| 内容記述タイプ | Abstract | |||||||||||||||||
| 内容記述 | [Author abstract]In the present paper, the authors have published the results of investigation about the effects of various paints in order to prevent corrosions and fouling organisms on metal materials in the sea. The metal panels treated with various paints were set up at three marine zones, which were beneath the sea water surface at 1.5 meters depth, the intertidal zone, and above the sea water surface. The composition, the preparation and the painting condition of anti-corrosive paints and anti-fouling paints were shown in Tables 1-7. The results of tests were given in Tables 8-10, Figs. 1-6, and Photos. 6,7. The most effective anti-fouling paints were firstly AF 5, AF 4 and secondly AF 10, AF 9. Anti-corrosive paints which had much anti-corrosion effects were an epoxy resin anti-corrosive paint. The anti-fouling effect did not coincide with the anti-corrosion effect in these paints. The paint which had both effects was E4 or E5 and this was an epoxy resin anti-corrosive paint coated with a vinyl chloride resin paint which contains tributyl tin fumarate, copper oleate or pentachlorophenol cupric salt, and organoarsenic compound.[著者抄録]本試験は厳しい条件下での暴露にもかかわらず、すぐれた結果が得られた。とくに防汚効力では有機スズと有機ヒ素および有機銅化合物を配合した薬剤が効果的であり、ついで50%亜酸化銅配合のものであった。防食効果はこれらの防汚効果と一致せず、塗膜の劣化状態と密接な関係にあった。波浪、光、酸素をどの影響が強く、それらの耐候性を必要とする干満帯での防錆塗料はエポキシ樹脂防錆塗料が効果的であり、海中浸漬ではタールウレタン系がやや効果的であった。防汚効果、防食効果いずれにも効果的配合はE4であり、トリプチルチンフマレートに有機ヒ素1T-67、オレイン酸銅配合のもので、エポキシ樹脂防錆塗料である。大気暴露試験では2年間の経過では、ほとんどのものは異常をきたさず、耐候性、防食性がすぐれており、ひき続き試験中である。本試験ですぐれた結果が得られたのは、基材の調整(みがき軟鋼板)、塗装回数(5回)、膜厚(150～500μ)、ほぼ均一な塗装 (ピンホールが少ない)、腐食促進因子(亜硫酸ガス、窒素酸化物など)の欠除などの寄与も無視できない。このことは逆に基材調整と塗装が適正であれば、塗膜の防食耐久性は存分に発揮されることを意味し、長期防食性を期すには塗料やその仕様の選択と同時に基材の十分な調整と入念な塗装が必要である。とくに本実験の主目的である冷却水用海洋構造物の防食防汚対策としての塗装には、構造表面のある程度の乾燥が必要であり、水分の除去とその塗装技術が重要な問題となってくる。この問題の解決のためには一例として構造物の内面に陸上で完全に塗装された金網(ある一定の大きさの網目で一定量の薬剤が流出するように工夫される)を内張して取替えるなどがあり、今後その点の施工上の研究が必要であると考える。 | |||||||||||||||||