Department of Mechanical Engineering, Faculty of Engineering, Kinki University
Department of Materials Chemistry, School of High-Technology for Human Welfare, Tokai University
Department of Mechanical Engineering, Faculty of Engineering, Kinki University
版
publisher
出版者 名前
近畿大学工学部
出版社 カナ
キンキ ダイガク コウガクブ
出版社 ローマ字
Kinki daigaku kogakubu
出版年(from)
2009
出版年(to)
12-21
日付 作成日
2010-05-20
雑誌名
近畿大学工学部研究報告
雑誌名(英)
Research reports of the Faculty of Engineering, Kinki University
号
43
ページ
55 - 60
発行年
2009-12-01
ISSN
0386491X
抄録
We have demonstrated in our previous report that the excess energy created during mechanical alloying (MA) yielded alloying of couples with negative mixing enthalpy and the new ternary bcc phase was formed. It was noticed that the important issue there was the structural correlation between the Laves phase and bcc structures. The aims of this study is to synthesize LaA1_2 based bcc alloys in structural relation to the Laves phase structure with additive element V, and to clarify the above issue on the structure and hydrogenation. The parent materials used in this study were La1_2 and V metal powders. The MA was performed under Ar gas atmosphere and the rotation speed is 710 rpm. The ratio of powder to ball weight is 1: 40. The results are summarized as follows: 1) We could not synthesis the single bcc phase from 60 hours of MA. After 60 hours of MA, amorphous phase was formed. 2) From the TEM bright image observation，we have confirmed that the alloy is composed by nano size particles such as 20 nm of diameter of crystalline particles. 3) The TDS was used to measure the hydride properties of the synthesized powders. The results showed that hydrogen was not absorbed after hydrogenation treatment.
<研究論文>メカニカルアロイング法を用いたLaAl系合金の創製とその水素親和性