木材-エポキシ樹脂接着体の疲労耐久性
https://kindai.repo.nii.ac.jp/records/5052
https://kindai.repo.nii.ac.jp/records/5052b5768edb-cab1-4a5b-b9ff-d94b18a8fc2d
| 名前 / ファイル | ライセンス | アクション |
|---|---|---|
AN00064044-19830315-0133.pdf (2.0 MB)
|
|
| Item type | ☆紀要論文 / Departmental Bulletin Paper(1) | |||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| 公開日 | 2008-01-28 | |||||||||||||||||
| タイトル | ||||||||||||||||||
| タイトル | 木材-エポキシ樹脂接着体の疲労耐久性 | |||||||||||||||||
| タイトル | ||||||||||||||||||
| タイトル | The durability of wood-epoxy resin bond system evaluated by fatigue test | |||||||||||||||||
| 言語 | en | |||||||||||||||||
| 著者 |
高谷, 政広
× 高谷, 政広
× 浜田, 良三
× 佐々木, 光
|
|||||||||||||||||
| 言語 | ||||||||||||||||||
| 言語 | jpn | |||||||||||||||||
| 資源タイプ | ||||||||||||||||||
| 資源タイプ識別子 | http://purl.org/coar/resource_type/c_6501 | |||||||||||||||||
| 資源タイプ | departmental bulletin paper | |||||||||||||||||
| 著者(英) | ||||||||||||||||||
| 言語 | en | |||||||||||||||||
| 値 | Takatani, Masahiro | |||||||||||||||||
| 著者(英) | ||||||||||||||||||
| 言語 | en | |||||||||||||||||
| 値 | Hamada, Ryozo | |||||||||||||||||
| 著者(英) | ||||||||||||||||||
| 言語 | en | |||||||||||||||||
| 値 | Sasaki, Hikaru | |||||||||||||||||
| 著者 所属 | ||||||||||||||||||
| 値 | 近畿大学農学部農芸化学科天然高分子研究室 | |||||||||||||||||
| 著者 所属 | ||||||||||||||||||
| 値 | 近畿大学農学部農芸化学科天然高分子研究室 | |||||||||||||||||
| 著者 所属 | ||||||||||||||||||
| 値 | 京都大学木材研究所 | |||||||||||||||||
| 著者所属(翻訳) | ||||||||||||||||||
| 値 | Laboratory of Natural High Polymer, Department of Agricultural Chemistry, Faculty of Agriculture, Kinki University | |||||||||||||||||
| 著者所属(翻訳) | ||||||||||||||||||
| 値 | Laboratory of Natural High Polymer, Department of Agricultural Chemistry, Faculty of Agriculture, Kinki University | |||||||||||||||||
| 著者所属(翻訳) | ||||||||||||||||||
| 値 | Wood Research Institute, Kyoto University | |||||||||||||||||
| 版 | ||||||||||||||||||
| 出版タイプ | NA | |||||||||||||||||
| 出版タイプResource | http://purl.org/coar/version/c_be7fb7dd8ff6fe43 | |||||||||||||||||
| 出版者 名前 | ||||||||||||||||||
| 出版者 | 近畿大学農学部 | |||||||||||||||||
| 書誌情報 |
近畿大学農学部紀要 en : Memoirs of the Faculty of Agriculture of Kinki University 号 16, p. 133-141, 発行日 1983-01-01 |
|||||||||||||||||
| ISSN | ||||||||||||||||||
| 収録物識別子タイプ | ISSN | |||||||||||||||||
| 収録物識別子 | 04538889 | |||||||||||||||||
| 抄録 | ||||||||||||||||||
| 内容記述タイプ | Abstract | |||||||||||||||||
| 内容記述 | [Author abstract]In order to know the durability of wood-epoxy bond system, cleavage fatigue tests with double cantilever type specimen and bending fatigue tests with crank type specimen were carried out. Fatigue strength (σ_7, M_7) and the ratio of fatigue strength to static strength (σ_7/σ_0,M_7/M_0) were determined by various fatigue tests, and the effect of flexibility of adhesives and thickness of glue-line on the fatigue properties were discussed. The results obtained were summarized as follows : (1) The stress concentration on the edge of glue-line was remarkably decreased with increasing flexibility of adhesives and water content of wood. (2) Cleavage fatigue strength decreased as increasing flexibility of adhesives, and maximum strength was obtained for the specimens bonded with straight epoxy resin (σ_7=3.0 kg/cm^2, σ_7/σ_0=0.66). (3) Bending fatigue strength under dry condition also decreased as increasing flexibility of adhesives, and good durability was obtained using straight epoxy adhesives at 1.5 mm thick of glue-line (M_7=200 kg・mm, M_7/M_0=0.33). (4) bending fatigue strength under wet condition seemed to be decreased with increasing flexibility of adhesives, and the tendency was not so clear compared with that in dry condition.[著者抄録]木材-エポキシ樹脂接着体の疲労耐久性を,二重片持ち梁試験片を用いる剥離疲労試験及びクランク型試験片を用いる板曲げ疲労試験によって評価した.接着剤のフレキシビリティ,グルーライン厚さ,及び木材含水率等を変化させて,接着層での応力緩和効果が異なる種々の接着体を作成し,これらの因子が接着体の疲労強度(σ_7)及び強度残存率(σ_7/σ_0)に与える影響を検討した.実験結果の概略は次のとおりである.(1)種々の接着剤及び接着層厚きで作成した2種類の疲労試験片について,接着層に発生する応力分布を計算した結果,チオコール添加量の異なる4種類のエポキシ樹脂接着剤,接着層厚さ及び木材含水率の相違等によって応力分散効果が顕著に変化した.(2)割裂き型試験片による剥離疲労耐久性は,フレキシビリティの大きい樹脂ほど耐久性の低下が大きくなる傾向が見られ,エポキシ単独樹脂(EP)で接着した試験体が最大の疲労強度と強度残存率を示した(σ_7=3.0kg/cm^2,σ_7/σ_0=0.66).(3)曲げ疲労試験における疲労耐久性においても,剥離疲労の場合とほぼ同様の劣化傾向が見られ,エポキシ単独樹脂を用いて厚さ1.5mmで接着された場合,強度の最大値が得られた(M_7=200 kg・mm, M_7/M_0=0.33).(4)湿潤での疲労耐久性においては,疲労によるM-N曲線の傾斜が乾燥状態のものに比べて緩やかであり,木材の可塑化による応力緩和の効果が顕著に認められた. | |||||||||||||||||