木材接着体の割裂試験における応力解析と割裂破壊靭性G_<IC>の測定
https://kindai.repo.nii.ac.jp/records/5045
https://kindai.repo.nii.ac.jp/records/50453fdd9cd0-e09a-420e-8e2c-01471b8e12d8
| 名前 / ファイル | ライセンス | アクション |
|---|---|---|
AN00064044-19840315-0035.pdf (1.3 MB)
|
|
| Item type | ☆紀要論文 / Departmental Bulletin Paper(1) | |||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| 公開日 | 2008-01-28 | |||||||||||||||||
| タイトル | ||||||||||||||||||
| タイトル | 木材接着体の割裂試験における応力解析と割裂破壊靭性G_<IC>の測定 | |||||||||||||||||
| タイトル | ||||||||||||||||||
| タイトル | Stress Analysis in Cleavage Test and Measurement of Cleavage Fracture Toughness G_<IC> of Wood-Adhesive Bond System | |||||||||||||||||
| 言語 | en | |||||||||||||||||
| 著者 |
高谷, 政広
× 高谷, 政広
× 浜田, 良三
× 佐々木, 光
|
|||||||||||||||||
| 言語 | ||||||||||||||||||
| 言語 | jpn | |||||||||||||||||
| 資源タイプ | ||||||||||||||||||
| 資源タイプ識別子 | http://purl.org/coar/resource_type/c_6501 | |||||||||||||||||
| 資源タイプ | departmental bulletin paper | |||||||||||||||||
| 著者(英) | ||||||||||||||||||
| 言語 | en | |||||||||||||||||
| 値 | Takatani, Masahiro | |||||||||||||||||
| 著者(英) | ||||||||||||||||||
| 言語 | en | |||||||||||||||||
| 値 | Hamada, Ryozo | |||||||||||||||||
| 著者(英) | ||||||||||||||||||
| 言語 | en | |||||||||||||||||
| 値 | Sasaki, Hikaru | |||||||||||||||||
| 著者 所属 | ||||||||||||||||||
| 値 | 近畿大学農学部農芸化学科天然高分子研究室 | |||||||||||||||||
| 著者 所属 | ||||||||||||||||||
| 値 | 近畿大学農学部農芸化学科天然高分子研究室 | |||||||||||||||||
| 著者 所属 | ||||||||||||||||||
| 値 | 京都大学木材研究所 | |||||||||||||||||
| 著者所属(翻訳) | ||||||||||||||||||
| 値 | Laboratory of Natural High Polymer, Department of Agricultural Chemistry, Faculty of Agriculture, Kinki University | |||||||||||||||||
| 著者所属(翻訳) | ||||||||||||||||||
| 値 | Laboratory of Natural High Polymer, Department of Agricultural Chemistry, Faculty of Agriculture, Kinki University | |||||||||||||||||
| 著者所属(翻訳) | ||||||||||||||||||
| 値 | Wood Research Institute, Kyoto University | |||||||||||||||||
| 版 | ||||||||||||||||||
| 出版タイプ | NA | |||||||||||||||||
| 出版タイプResource | http://purl.org/coar/version/c_be7fb7dd8ff6fe43 | |||||||||||||||||
| 出版者 名前 | ||||||||||||||||||
| 出版者 | 近畿大学農学部 | |||||||||||||||||
| 書誌情報 |
近畿大学農学部紀要 en : Memoirs of the Faculty of Agriculture of Kinki University 号 17, p. 35-42, 発行日 1984-01-01 |
|||||||||||||||||
| ISSN | ||||||||||||||||||
| 収録物識別子タイプ | ISSN | |||||||||||||||||
| 収録物識別子 | 04538889 | |||||||||||||||||
| 抄録 | ||||||||||||||||||
| 内容記述タイプ | Abstract | |||||||||||||||||
| 内容記述 | [Author abstract]In order to obtain fundamental data for reasonable adhesive joint's plannings of wood construction, stress distribution of double cantilever beam type specimens for measuring the cleavage fracture toughness of wood-adhesive bond system was calculated numerically by Finite Element Method. Fracture tests were made on the specimens of buna-epoxy resin bond system with different thickness and flexibilities of glue-line, and also the other specimens of wood-adhesive bond system using two kinds of wood species and nine adhesives. Fracture toughness G_<IC> for each specimens was calculated. Next results were obtained. 1) It was shown by the numerical analysis (stress distribution) that stress concentration at the crack tip of specimen decreased with increasing flexibility of epoxy resin and thickness of glue-line. It was speculated that good bond strength was obtained by the combinations of rigid adherends and flexible adhesives. 2) G_<IC> of buna-epoxy bond system increased with increasing flexibility and thickness of glueline, and the maximum value 1.10 kg・cm/cm^2 was obtained by using epoxy adhesives of 60 phr amount of Thiokol at 1.5mm thick of glue-line. 3) As to the influence of mechanical properties of adherends on G_<IC>, generally it was concluded that dc could be improved by using rigid adherends when adhesive was flexible, and also by using flexible adherends when adhesive was rigid. 4) The results of measurement of G_<IC>, (2) and (3), corresponded well to the ones of stress analysis, (1).[著者抄録]フレキシビリティーが自由に変えられるエポキシ樹脂と9種類の市販接着剤を用いて作製した二重片持はりタイプの木材接着試験片について有限要素法による応力解析と割裂破壊靭性G_<IC>の測定を行なった.結果の概要は次のとおりである.(1)応力解析の結果,エポキシ樹脂のフレキシビリティーと接着層の厚さが増加すると共に試験片の接着層端での応力分散の効果が顕著になった.イチイガシ,ブナなどの硬い被着材には,エポキシ樹脂にフレキシビライザーを40phr及び60phr添加した軟性のある接着剤(TL-40及びTL-60)を組み合わせると接着強度が大きくなると推測された.(2)ブナーエポキシ樹脂接着体のG_<IC>の値は,接着層の厚さとフレキシビリティーの増加と共に増大した.最大のG_<IC>の値(1.10kg・cm/cm^2)はTL-60の接着剤で接着した接着層の厚さ1.5mmの試験体で得られた.(3)9種類の市販の接着剤で接着したブナ及びスブルース材のG_<IC>の値についてみると,柔軟性のあるポリ酢酸ビニルやα-オレフィン系の接着剤を用いた場合,硬い木材(ブナ)の接着体の方がG_<IC>の値が大きくなり,逆に硬いフェノールやエポキシ系の接着剤には軟らかい木材(スプルース)を用いた方がG_<IC>の値が大きくなった.(4)(2)と(3)のG_<IC>の測定の結果は(1)の応力解析より推定される結果とよく一致する. | |||||||||||||||||