 note = {研究成果の概要（和文）：C/C材／Ni基耐熱超合金の異材間高品位接合用高融点Ni基合金を試作した結果，C/C材とInconel-600に対し58Ni-20Cr-22Si合金と57Ni-20Cr-22Si が良好なぬれを示した．これら合金は液相線温度が1200℃以下で高温ろう付が可能である．C/C材／Inconel-600接合体は界面のC/C材内部でき裂が観察された．継手強度はCTE値差による残留熱応力が生じるがNb箔を挿入することにより改善することが示された．C/C材，Inconel-600と合金層の界面接合は良好であるため，C/C材／Inconel-600を高品位に接合可能と考えられる．
研究成果の概要（英文）：For C/C composites/Ni-based refractory metal high quality joining, Ni-based alloy was made. 58Ni-20Cr-22Si alloy and 57Ni-20Cr-22Si alloy had good wettability on both C/C composites and Inconel-600 Ni-base alloy. These Ni-base alloy had the liquidus temperature lower than 1200ºC and can be used for high temperature brazing. The shear strength of C/C composites/Inconel-600 brazed joint with these metals was 2MPa. Crack was observed in C/C composites near joint interface. Enhancement of joint strength is considered to be due to the residual stress by CTE value difference between C/C composites and Inconel-600. By inserting Nb foil in the mating surfaces, the joint strength was improved. The interfacial bonding is, however, sound between both C/C composites and these alloys and Inconel-600 and these alloys, and with these alloys, high quality bonding is considered to be able to achieve., 研究種目：基盤研究(C);  研究期間：2012～2015;   課題番号：24560126;   研究分野：接合工学;   科研費の分科・細目：, application/pdf},
 title = {炭素繊維強化複合材料と耐熱超合金の金属中間層を用いた高品位異材接合},
 year = {2016},
 yomi = {イケショウジ, トシタカ}
}